PRO-SET Technical Data Summary
Pro-Set Technical Data Summary
Resin |
117LV |
125 |
||||||||||
Hardener |
224 |
226 |
229 |
237 |
239 |
224 |
226 |
229 |
237 |
239 |
||
Handling Characteristics |
Mixed Viscosity at RT* | 800 cps | 350 cps | 310 cps | 360 cps | 290 cps | 1400 cps | 675 cps | 450 cps | 725 cps | 600 cps | |
| Mixing Ratio by Weight | 100:33 | 100:30 | 100:31 | 100:30 | 100:31 | 100:31 | 100:29 | 100:30 | 100:29 | 100:30 | ||
| 100 g Pot Life at RT* | 21 min. | 44 min. | 110 min. | 281 min. | 465 min. | 20 min. | 37 min. | 77 min. | 240 min. | 360 min. | ||
RT* Cure 2 weeks |
Tensile Strength (psi) | 9911 | 8234 | 8231 | NA** | NA** | 10077 | 7960 | 7550 | NA** | NA** | |
| Tensile Modulus (psi) | 4.7E+5 | 5.2E+5 | 5.2E+5 | NA** | NA** | 5.3E+5 | 5.3E+5 | 5.1E+5 | NA** | NA** | ||
| Heat Deflection Temp. F | 135 | 129 | 118 | NA** | NA** | 127 | 123 | 122 | NA** | NA** | ||
RT* 15 hr. + 140 deg. F 8 hr. |
Tensile Strength (psi) | 11161 | 10708 | 10101 | 10015 | 9582 | 11269 | 10386 | 10247 | 8893 | 8683 | |
| Tensile Modulus (psi) | 5.3E+5 | 5.0E+5 | 4.9E+5 | 5.2E+5 | 4.6E+5 | 5.0E+5 | 4.5E+5 | 4.5E+5 | 5.0E+7 | 4.8E+5 | ||
| Heat Deflection Temp. F | 147 | 156 | 133 | 154 | 147 | 166 | 140 | 143 | 155 | 148 | ||
RT* 15 hr. + 180 deg. F 8 hr. |
Tensile Strength (psi) | 11037 | 11683 | 10064 | 10474 | 9824 | 10297 | 11071 | 9974 | 11151 | 9824 | |
| Tensile Modulus (psi) | 5.2E+5 | 4.7E+5 | 4.9E+5 | 4.8E+5 | 4.5E+5 | 4.6E+5 | 4.3E+5 | 4.2E+5 | 4.9E+5 | 4.3E+5 | ||
| Heat Deflection Temp. F | 148 | 177 | 142 | 184 | 176 | 161 | 172 | 157 | 189 | 179 | ||
Resin |
135 |
145 |
||||||||||
Hardener |
224 |
226 |
229 |
237 |
239 |
224 |
226 |
229 |
237 |
239 |
||
Handling Characteristics |
Mixed Viscosity at RT* | 2475 cps | 1350 cps | 950 cps | 1200 cps | 675 cps | 3800 cps | 1225 cps | 1055 cps | 1800 cps | 1330 cps | |
| Mixing Ratio by Weight | 100:27 | 100:25 | 100:26 | 100:25 | 100:26 | 100:29 | 100:27 | 100:28 | 100:28 | 100:28 | ||
| 100 g Pot Life at RT* | 18 min | 31 min. | 59 min. | 113 min. | 146 min. | 18 min. | 31 min. | 67 min. | 155 min. | 268 min. | ||
RT* Cure 2 weeks |
Tensile Strength (psi) | 9842 | 8036 | 6505 | NA** | NA** | NA** | NA** | NA** | NA** | NA** | |
| Tensile Modulus (psi) | 5.2E+5 | 5.4E+5 | 5.4E+5 | NA** | NA** | NA** | NA** | NA** | NA** | NA** | ||
| Heat Deflection Temp. F | 135 | 125 | 122 | NA** | NA** | NA** | NA** | NA** | NA** | NA** | ||
RT* 15 hr. + 140 deg. F 8 hr. |
Tensile Strength (psi) | 11744 | 8629 | 9091 | 9933 | 10769 | 11501 | 10781 | 10417 | 10572 | 10622 | |
| Tensile Modulus (psi) | 5.1E+5 | 5.5E+5 | 5.1E+5 | 5.1E+5 | 4.9E+5 | 5.3E+5 | 4.7E+5 | 4.5E+5 | 5.3E+5 | 4.8E+5 | ||
| Heat Deflection Temp. F | 163 | 149 | 138 | 172 | 162 | 162 | 165 | 154 | 159 | 169 | ||
RT* 15 hr. + 180 deg. F 8 hr. |
Tensile Strength (psi) | 10601 | 10007 | 10397 | 10874 | 11163 | 11181 | 11801 | 10979 | 10534 | 10151 | |
| Tensile Modulus (psi) | 5.1E+5 | 5.2E+5 | 5.2E+5 | 5.1E+5 | 4.3E+5 | 4.7E+5 | 3.9E+5 | 3.3E+5 | 5.6E+5 | 4.7E+5 | ||
| Heat Deflection Temp. F | 166 | 167 | 154 | 196 | 198 | 182 | 206 | 213 | 197 | 200 | ||
September 2007
Please visit the Pro-Set Epoxy website at www.prosetepoxy.com for more complete information.
*Room Temperature (RT) 70-75 degrees F.
** Data not available as this combination requires post cure.
This information has been furnished by the manufacturer and represents typical values; not to be construed as specifications. CST-The Compsites Store, Inc., their principals and/or agents, accept no liability for any damages, including personal injury and/or property damage, resulting from intentional or unintentional use of these products. Purchaserand /or user of the products assumes all risks and liability in the use of these products and shall have no claim against the above named company, their owers, princpals or agents whatsoever.